增强品级

MVR (300℃/1.2kg)6.0cm³/10min;10%Glass fibre filled;flame retarded;UL94V0/1.5mm and 5VA/3.0mm;;high viscosity;easy release;injection molding;melt temperature 280-320℃; available in opaque colors only

体积熔融指数 (300℃ /1.2kg)6.0cm³/10min；玻纤含量 10%；阻燃改善等级；阻燃等 级 UL94V0/1.5mm，5VA/3.0mm；易脱模；高粘度，注塑等级；熔融加工温度区间为280-320℃；可供应实色

MVR (300℃/1.2kg) 6.0cm³/10min; 10%Glass fibre filled;UV stabilized;flame retarded UL94V0/1.5mm and 5VA/3.0mm; high viscosity; easy release; injection molding; melt temperature 280– 320℃; available in opaque colors only

体积熔融指数 (300℃ /1.2kg)6.0cm³/10min; 玻纤含量 10%; 抗紫外线改善等级 ; 阻燃 改善等级 ; 阻燃等级 UL94V0/1.5mm,5VA/3.0mm; 易脱模 ; 高粘度，注塑等级 ; 熔融加工温度区间为 280-320℃ ; 可供应实色

MVR(300℃/1.2kg)15.0cm/10min;10%Glass fibre filled;fame retarded; UL94V0/1.2mm and 5VA/3.0mm; low viscosity; easy release; injection molding ;melt temperature 280 -320℃; available in opaque colors only

体积熔融指数 (300℃ /1.2kg)15.0cm³/10min；玻纤含量 10%；流动性改善等级；阻 燃改善等级；阻燃等级 UL94V0/1.2mm,5VA/3.0mm；易脱模；较低粘度，注塑等级；熔融加工温度区间为 280-320℃ ; 可供应实色

MVR (300℃/1.2kg)5.0cm³/10min;20%Glass fibre filled;flame retarded;UL94V0/1.5mm and 5VA/3.0mm;high viscosity;easy release;injection molding ;melt temperature 280 -320℃; available in opaque colors only

体积熔融指数 (300℃ /1.2kg)5.0cm³/10min; 玻纤含量 20%; 阻燃改善等级 ; 阻燃等级 UL94V0/1.5mm,5VA/3.0mm; 易脱模 ; 高粘度，注塑等级 ; 熔融加工温度区间为 280-320℃ ; 可供应实色

MVR(300℃/1.2kg)16.0cm³/10min;20% Glass fibre filled;Flow ability improved;

UL94HB/1.5mm,low viscosity; easy release; injection molding; melt temperature 280-320℃ available in opaque colors only

体积熔融指数 (300℃ /1.2kg)16.0cm³/10min; 玻纤含量 20%; 流动性改善等级 ; 阻燃等级 UL94HB/1.5mm; 易脱模；较低粘度，注塑等级 ; 熔融加工温度区间为 280-320℃ ; 可供应实色

MVR(300℃/1.2kg)10.0cm³/10min;10%Glass fibre filled;impact modified; UL94HB/0.75mm; low viscosity; easy release; injection molding;melt temp erature280-320℃; available in opaque colors only

体积熔融指数 (300℃ /1.2kg)10.0cm³/10min; 玻纤含量 10%; 抗冲击改善等级 ; 阻燃UL94HB/0.75mm；易脱模；中等粘度，注塑等级；熔融加工温度区间为 280-320℃ ;可供应实色

MVR(300℃/1.2kg)10.0cm³/10min;20%Glass fibre filled;impact modified;UL94HB/0.75mm medium viscosity; easy release; injection molding ;melt temperature 280-320℃; available in opaque colors only 280-320℃; available in opaque colors only

体积熔融指数 (300℃ /1.2kg)10.0cm³/10min; 玻纤含量 20%; 抗冲击改善等级 ; 阻燃UL94HB/0.75mm; 易脱模 ; 中等粘度，注塑等级 ; 熔融加工温度区间为 280-320℃ ; 可供应实色

MVR(300℃/1.2kg)9.0cm³/10min;30%Glass fibre filled;impact modified;UL94HB/0.75mm medium viscosity; easy release; injection molding ;melt temperature 280-320 ℃; available in opaque colors only

体积熔融指数 (300℃ /1.2kg)9.0cm³/10min; 玻纤含量 30%; 抗冲击改善等级 ; 阻燃UL94HB/0.75mm; 易脱模 ; 中等粘度，注塑等级 ; 熔融加工温度区间为 280-320℃ ;可供应实色